Liquid crystal compounds

ABSTRACT

The invention relates to liquid crystal compounds of formula (1), where X 1 , X 2 , X 3 , Z 1 , Z 2 , L 1 , L 2 , L 3 , L 4 , L 5 , L 6 , L 7 , L 8 , L 9 , L 10 , L 11  and a have the meanings given in claim  1,  and liquid crystal media containing at least one compound of formula (I) and electro-optical displays comprising such a liquid crystal medium.

[0001] The present invention relates to liquid-crystalline compounds and to a liquid-crystalline medium, to the use thereof for electro-optical purposes, and to displays containing this medium.

[0002] Liquid crystals are used principally as dielectrics in display devices, since the optical properties of such substances can be modified by an applied voltage. Electro-optical devices based on liquid crystals are extremely well known to the person skilled in the art and can be based on various effects. Examples of such devices are cells having dynamic scattering, DAP (deformation of aligned phases) cells, guest/host cells, TN cells having a twisted nematic structure, STN (supertwisted nematic) cells, SBE (super-birefringence effect) cells and OMI (optical mode interference) cells. The commonest display devices are based on the Schadt-Helfrich effect and have a twisted nematic structure.

[0003] The liquid-crystal materials must have good chemical and thermal stability and good stability to electric fields and electromagnetic radiation. Further-more, the liquid-crystal materials should have low viscosity and produce short addressing times, low threshold voltages and high contrast in the cells.

[0004] They should furthermore have a suitable mesophase, for example a nematic or cholesteric mesophase for the above-mentioned cells, at the usual operating temperatures, i.e. in the broadest possible range above and below room temperature. Since liquid crystals are generally used as mixtures of a plurality of components, it is important that the components are readily miscible with one another. Further properties, such as the electrical conductivity, the dielectric anisotropy and the optical anisotropy, have to satisfy various requirements depending on the cell type and area of application. For example, materials for cells having a twisted nematic structure should have positive dielectric anisotropy and low electrical con-ductivity.

[0005] For example, for matrix liquid-crystal displays with integrated non-linear elements for switching individual pixels (MLC displays), media having large positive dielectric anisotropy, broad nematic phases, relatively low birefringence, very high specific resistance, good UV and temperature stability and low vapour pressure are desired.

[0006] Matrix liquid-crystal displays of this type are known. Non-linear elements which can be used for individual switching of the individual pixels are, for example, active elements (i.e. transistors). The term “active matrix” is then used, where a distinction can be made between two types:

[0007] 1. MOS (metal oxide semiconductor) or other diodes on a silicon wafer as substrate.

[0008] 2. Thin-film transistors (TFTs) on a glass plate as substrate.

[0009] The use of single-crystal silicon as substrate material restricts the display size, since even modular assembly of various part-displays results in problems at the joins.

[0010] In the case of the more promising type 2, which is preferred, the electro-optical effect used is usually the TN effect. A distinction is made between two technologies: TFTs comprising compound semiconductors, such as, for example, CdSe, or TFTs based on polycrystalline or amorphous silicon. Intensive work is being carried out world-wide on the latter technology.

[0011] The TFT matrix is applied to the inside of one glass plate of the display, while the other glass plate carries the transparent counterelectrode on its inside. Compared with the size of the pixel electrode, the TFT is very small and has virtually no adverse effect on the image. This technology can also be extended to fully colour-capable displays, in which a mosaic of red, green and blue filters is arranged in such a way that a filter element is opposite each switchable pixel.

[0012] The TFT displays usually operate as TN cells with crossed polarisers in transmission and are illuminated from the back.

[0013] The term MLC displays here covers any matrix display with integrated non-linear elements, i.e., besides the active matrix, also displays with passive elements, such as varistors or diodes (MIM=metal-insulator-metal).

[0014] MLC displays of this type are particularly suitable for TV applications (for example pocket television sets) or for high-information displays for computer applications (laptops) and in automobile or aircraft construction. Besides problems regarding the angle dependence of the contrast and the response times, difficulties also arise in MLC displays due to insufficiently high specific resistance of the liquid-crystal mixtures [TOGASHI, S., SEKIGUCHI, K., TANABE, H., YAMAMOTO, E., SORIMACHI, K., TAJIMA, E., WATANABE, H., SHIMIZU, H., Proc. Eurodisplay 84, September 1984: A 210-288 Matrix LCD Controlled by Double Stage Diode Rings, p. 141 if, Paris; STROMER, M., Proc. Eurodisplay84, September 1984: Design of Thin Film Transistors for Matrix Addressing of Television Liquid Crystal Displays, p. 145 ff, Paris]. With decreasing resistance, the contrast of an MLC display deteriorates, and the problem of after-image elimination may occur. Since the specific resistance of the liquid-crystal mixture generally drops over the life of an MLC display owing to interaction with the interior surfaces of the display, a high (initial) resistance is very important in order to obtain acceptable service lives. In particular in the case of low-volt mixtures, it was hitherto impossible to achieve very high specific resistance values. It is furthermore important that the specific resistance exhibits the smallest possible increase with increasing temperature and after heating and/or UV exposure. The low-temperature properties of the mixtures from the prior art are also particularly disadvantageous. It is demanded that no crystallisation and/or smectic phases occur, even at low temperatures, and the temperature dependence of the viscosity is as low as possible. The MLC displays from the prior art thus do not meet today's requirements.

[0015] There thus continues to be a great demand for MLC displays having very high specific resistance at the same time as a large working-temperature range, short response times even at low temperatures and low threshold voltage which do not have these disadvantages, or only do so to a reduced extent.

[0016] In TN (Schadt-Helfrich) cells, media are desired which facilitate the following advantages in the cells:

[0017] extended nematic phase range (in particular down to low temperatures)

[0018] the ability to switch at extremely low temperatures (outdoor use, auto-mobile, avionics)

[0019] increased resistance to UV radiation (longer service life)

[0020] high Δn for faster response times

[0021] The media available from the prior art do not allow these advantages to be achieved while simultaneously retaining the other parameters.

[0022] In the case of supertwisted (STN) cells, media are desired which enable greater multiplexability and/or lower threshold voltages and/or broader nematic phase ranges (in particular at low temperatures). To this end, a further widening of the available parameter latitude (clearing point, smec-tic-nematic transition or melting point, viscosity, dielectric parameters, elastic parameters) is urgently desired.

[0023] The invention has the object of providing media, in particular for MLC, IPS, TN or STN displays of this type, which do not have the above-mentioned disadvantages or only do so to a reduced extent, and preferably simultaneously have very high specific resistance values and low threshold voltages. This object requires liquid-crystalline compounds which have a high clearing point and low rotational viscosity.

[0024] It has now been found that this object can be achieved if the liquid-crystalline compounds according to the invention are used.

[0025] The invention thus relates to liquid-crystalline compounds of the formula I

[0026] in which

[0027] X¹ and X² are each, independently of one another, F, Cl, Br or I, or one of the radicals X¹ and X² is alternatively H,

[0028] X³ is F, Cl, CN, NCS, SF₅, or a halogenated alkyl, alkoxy, alkenyl or alkenyloxy radical having up to 5 carbon atoms,

[0029] Z¹ and Z² are each, independently of one another, —CO—O—, —O—CO—, —CF₂O—, —OCF₂—, —CH₂O—, —OCH₂—, —CH₂CH₂—, —(CH₂)₄—, —C₂F₄—, —CH₂CF₂—, —CF₂CH₂—, —CF═CF—, —CH═CH—, —C≡C— or a single bond, with the proviso that at least one of the bridges Z¹ and Z² is —CF₂O—or —OCF₂—,

[0030] a is 0, 1 or 2, and

[0031] L¹ to L¹¹ are each, independently of one another, H or F.

[0032] The invention furthermore relates to the use of the compounds of the formula I in liquid-crystalline media, as synthetic building blocks, for example for liquid crystals, crop-protection agents and pharmaceuticals. Particular preference is given to compounds where X¹ and/or X²═Cl, Br or I, in particular where Br and I.

[0033] The compounds of the formula I have a broad range of applications. Depending on the choice of substituents, these compounds can serve as base materials of which liquid-crystalline media are predominantly composed; however, it is also possible to add compounds of the formula I to liquid-crystalline base materials from other classes of compound in order, for example, to modify the dielectric and/or optical anisotropy of a dielectric of this type and/or in order to optimise its threshold voltage and/or its viscosity.

[0034] In the pure state, the compounds of the formula I are colourless and form liquid-crystalline mesophases in a temperature range which is favourably located for electro-optical use. In particular, the compounds according to the invention are distinguished by their broad nematic phase range. In liquid-crystalline mixtures, the substances according to the invention suppress the smectic phases and result in a significant improvement in the low-temperature storage stability. They are stable chemically, thermally and to light.

[0035] The invention relates, in particular, to the compounds of the formula I in which X¹ is F or Cl, X²═H and X³═F or OCF₃.

[0036] Particular preference is given to compounds of the formula I in which a=1, furthermore a=2. Z¹ or Z² is preferably a single bond, furthermore —CF₂O—, —OCF₂—, —C₂F₄—, —CH₂O—, —OCH₂— or —COO—.

[0037] L¹ is preferably F and L² is preferably H or F. L¹ and L² are particularly preferably fluorine. Preference is furthermore given to compounds in which L² and L³ are fluorine.

[0038] Particularly preferred compounds of the formula I are the compounds I1 to I120:

[0039] The compounds of the formula I are prepared by methods known per se, as described in the literature (for example in the standard works, such as Houben-Weyl, Methoden der organischen Chemie [Methods of Organic Chemistry], Georg-Thieme-Verlag, Stuttgart), to be precise under reaction conditions which are known and suitable for the said reactions. Use can also be made here of variants which are known per se, but are not mentioned here in greater detail.

[0040] The compounds according to the invention can be prepared, for example, as follows:

[0041] The compounds according to the invention are also suitable as synthetic building blocks for liquid crystals, as can be seen, for example, from Scheme 4.

[0042] The invention also relates to electro-optical displays (in particular STN or MLC displays having two plane-parallel outer plates, which, together with a frame, form a cell, integrated non-linear elements for switching individual pixels on the outer plates, and a nematic liquid-crystal mixture of positive dielectric anisotropy and high specific resistance which is located in the cell) which contain media of this type, and to the use of these media for electro-optical purposes.

[0043] The liquid-crystal mixtures according to the invention enable a significant widening of the available parameter latitude.

[0044] The achievable combinations of clearing point, viscosity at low temperature, thermal and UV stability and dielectric anisotropy are far superior to previous materials from the prior art.

[0045] The requirement for a high clearing point, a nematic phase at low temperature and a high Δε has hitherto only been satisfied to an inadequate extent. Although liquid-crystal mixtures such as, for example, MLC-6476 and MLC-6625 (Merck KGaA, Darmstadt, Germany) have comparable clearing points and low-temperature stabilities, they have, however, relatively high Δn values and also higher threshold voltages of about ≧1.7 V.

[0046] Other mixture systems have comparable viscosities and Δε values, but only have clearing points in the region of 60° C.

[0047] The liquid-crystal mixtures according to the invention, while retaining the nematic phase down to −20° C. and preferably down to −30° C., particularly preferably down to 40° C., enable clearing points above 80°, preferably above 90°, particularly preferably above 100° C., simultaneously dielectric anisotropy values Δε of ≧4, preferably ≧6, and a high value for the specific resistance to be achieved, enabling excellent STN and MLC displays to be obtained. In particular, the mixtures are characterised by low operating voltages. The TN thresholds are below 1.5 V, preferably below 1.3 V.

[0048] It goes without saying that, through a suitable choice of the components of the mixtures according to the invention, it is also possible for higher clearing points (for example above 110°) to be achieved at a higher threshold voltage or lower clearing points to be achieved at lower threshold voltages with retention of the other advantageous properties. At viscosities correspondingly increased only slightly, it is likewise possible to obtain mixtures having greater Δε and thus lower thresholds. The MLC displays according to the invention preferably operate at the first Gooch and Tarry transmission minimum [C. H. Gooch and H. A. Tarry, Electron. Left. 10, 2-4, 1974; C. H. Gooch and H. A. Tarry, AppI. Phys., Vol. 8, 1575-1584,1975], where, besides particularly favourable electro-optical properties, such as, for example, high steepness of the characteristic line and low angle dependence of the contrast (German Patent 30 22 818), a lower dielectric anisotropy is sufficient at the same threshold voltage as in an analogous display at the second minimum. This enables significantly higher specific resistance values to be achieved using the mixtures according to the invention at the first minimum than in the case of mixtures comprising cyano compounds. Through a suitable choice of the individual components and their proportions by weight, the person skilled in the art is able to set the birefringence necessary for a pre-specified layer thickness of the MLC display using simple routine methods.

[0049] The flow viscosity ν₂₀ at 20° C. is preferably <60 mm²·S⁻¹, particularly preferably <50 mm²·s⁻¹. The nematic phase range is preferably at least 90°, in particular at least 100°. This range preferably extends at least from −30° to +80°.

[0050] Measurements of the capacity holding ratio (HR) [S. Matsumoto et al., Liquid Crystals 5, 1320 (1989); K. Niwa et al., Proc. SID Conference, San Francisco, June 1984, p. 304 (1984); G. Weber et al., Liquid Crystals 5, 1381 (1989)] have shown that mixtures according to the invention comprising compounds of the formula I exhibit a significantly smaller decrease in the HR with increasing temperature than analogous mixtures comprising cyanophenylcyclohexanes of the formula

[0051] or esters of the formula

[0052] instead of the compounds of the formula I.

[0053] The UV stability of the mixtures according to the invention is also considerably better, i.e. they exhibit a significantly smaller decrease in the HR on exposure to UV.

[0054] The media according to the invention are preferably based on a plurality of (preferably two, three or more) compounds of the formula 1, i.e. the proportion of these compounds is 5-95%, preferably 10-60% and particularly preferably in the range 15-40%.

[0055] The individual compounds of the formulae I to IX and their sub-formulae which can be used in the media according to the invention are either known or they can be prepared analogously to the known compounds.

[0056] Preferred embodiments are indicated below:

[0057] The medium preferably comprises one, two or three homologous compounds of the formula I, where each homologue is present in the mixture up to a maximum amount of 10%.

[0058] Medium additionally comprises one or more compounds selected from the group consisting of the general formulae II to IX:

[0059] in which the individual radicals have the following meanings:

[0060] R⁰ H, n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 carbon atoms,

[0061] X⁰ F, Cl, halogenated alkyl, halogenated alkenyl, halogenated alkenyloxy or halogenated alkoxy having up to 7 carbon atoms,

[0062] Z⁰ —CH═CH—, —C₂H₄—, —(CH₂)₄—, —C₂F₄—, —CH₂O—, —OCH₂—, —CF═CF—, —CF₂O—, —OCF₂—or —COO—,

[0063] Y¹, Y², Y³ and Y⁴ each, independently of one another, H or F, and

[0064] r 0 or 1.

[0065] The compound of the formula IV is preferably

[0066] The medium preferably comprises one or more compounds of the formulae

[0067] in which R⁰ and Y² are as defined above.

[0068] The medium preferably comprises one, two or three, furthermore four, homologues of the compounds selected from the group consisting of H1 to H18 (n=1-7):

[0069] The medium additionally comprises one or more compounds selected from the group consisting of the general formulae X to XV:

[0070] in which R⁰, X⁰, Y¹, Y², Y³ and Y⁴ each, independently of one another, have one of the meanings indicated in claim 7. X⁰ is preferably F, Cl, CF₃, OCF₃ or OCHF₂. R⁰ is preferably H, alkyl,oxaalkyl, fluoroalkyl, alkenyl or alkenyloxy.

[0071] The proportion of compounds of the formulae I to IX together in the mixture as a whole is at least 50% by weight.

[0072] The proportion of compounds of the formula I in the mixture as a whole is from 5 to 50% by weight.

[0073] The proportion of compounds of the formulae II to IX in the mixture as a whole is from 30 to 70% by weight.

[0074] The medium comprises compounds of the formulae II, III, IV, V, VI, VII, VIII and/or IX.

[0075] R⁰ is straight-chain alkyl or alkenyl having from 2 to 7 carbon atoms.

[0076] The medium essentially consists of compounds of the formulae I to XV.

[0077] The medium comprises further compounds, preferably selected from the following group consisting of the general formulae XVI to XX:

[0078] in which R⁰ and X⁰ are as defined above, and the 1,4-phenylene rings may be substituted by CN, chlorine or fluorine. The 1,4-phenylene rings are preferably mono- or polysubstituted by fluorine atoms.

[0079] The medium comprises further compounds, preferably selected from the following group consisting of the formulae RI to RIX

[0080] in which

[0081] R⁰ is n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 carbon atoms,

[0082] d is 0, 1 or 2,

[0083] Y¹ is H or F,

[0084] alkyl and

[0085] alkyl* are each, independently of one another, a straight-chain or branched alkyl radical having 1-9 carbon atoms,

[0086] alkenyl and

[0087] alkenyl* are each, independently of one another, a straight-chain or branched alkenyl radical having up to 9 carbon atoms.

[0088] The medium preferably comprises one or more compounds of the formulae

[0089] in which n and m are each an integer from 1 to 9.

[0090] The I: (II+III+IV+V+VI+VII+VIII+IX) weight ratio is preferably from 1:10 to 10:1.

[0091] The medium essentially consists of compounds selected from the group consisting of the general formulae I to XV.

[0092] It has been found that even a relatively small proportion of compounds of the formula I mixed with conventional liquid-crystal materials, but in particular with one or more compounds of the formula II, III, IV, V, VI, VII, VIII or IX, results in a considerable lowering of the threshold voltage and in low birefringence values, with broad nematic phases with low smectic-nematic transition temperatures being observed at the same time, improving the storage stability. The compounds of the formulae I to IX are colourless, stable and readily miscible with one another and with other liquid-crystal materials.

[0093] The term “alkyl” or “alkyl*” covers straight-chain and branched alkyl groups having 1-9 carbon atoms, in particular the straight-chain groups methyl, ethyl, propyl, butyl, pentyl, hexyl and heptyl. Groups having 2-5 carbon atoms are generally preferred.

[0094] The term “alkenyl” or “alkenyl*” covers straight-chain and branched alkenyl groups having up to 9 carbon atoms, in particular the straight-chain groups. Particularly preferred alkenyl groups are C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl, C₅-C₇-4-alkenyl, C₆-C₇-5-alkenyl and C₇-6-alkenyl, in particular C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl and C₅-C₇-4-alkenyl. Examples of preferred alkenyl groups are vinyl, 1E-propenyl, 1E-butenyl, 1E-pentenyl, 1E-hexenyl, 1E-heptenyl, 3-butenyl, 3E-pentenyl, 3E-hexenyl, 3E-heptenyl, 4-pentenyl, 4Z-hexenyl, 4E-hexenyl, 4Z-heptenyl, 5-hexenyl, 6-heptenyl and the like. Groups having up to 5 carbon atoms are generally preferred.

[0095] The term “fluoroalkyl” preferably covers straight-chain groups having a terminal fluorine, i.e. fluoromethyl, 2-fluoroethyl, 3-fluoropropyl, 4-fluoro-butyl, 5-fluoropentyl, 6-fluorohexyl and 7-fluoroheptyl. However, other positions of the fluorine are not excluded.

[0096] The term “oxaalkyl” preferably covers straight-chain radicals of the formula C_(n)H_(2n+1)—O—(CH₂)_(m), in which n and m are each, independently of one another, from 1 to 6. Preferably, n=1 and m is from 1 to 6.

[0097] Through a suitable choice of the meanings of R⁰ and X⁰, the addressing times, the threshold voltage, the steepness of the transmission characteristic lines, etc., can be modified in the desired manner. For example, 1E-alkenyl radicals, 3E-alkenyl radicals, 2E-alkenyloxy radicals and the like generally result in shorter addressing times, improved nematic tendencies and a higher ratio of the elastic constants k₃₃ (bend) and k₁₁ (splay) compared with alkyl or alkoxy radicals. 4-Alkenyl radicals, 3-alkenyl radicals and the like generally give lower threshold voltages and smaller values of k₃₃/k₁₁ compared with alkyl and alkoxy radicals.

[0098] A —CH₂CH₂— group in Z¹ and/or Z² generally results in higher values of k₃₃/k₁₁ compared with a single covalent bond. Higher values of k₃₃/k₁₁ facilitate, for example, flatter transmission characteristic lines in TN cells with a 90° twist (in order to achieve grey shades and faster response times) and steeper transmission characteristic lines in STN, SBE and OMI cells (greater multiplexability), and vice versa.

[0099] The optimum mixing ratio of the compounds of the formulae I and II+III+IV+V+VI+VII+VIII+IX depends substantially on the desired properties, on the choice of the components of the formulae I, II, III, IV, V, VI, VII, VIII and/or IX, and on the choice of any further components that may be present. Suitable mixing ratios within the range given above can easily be determined from case to case.

[0100] The total amount of compounds of the formulae I to XV in the mixtures according to the invention is not crucial. The mixtures can therefore comprise one or more further components for the purposes of optimisation of various properties. However, the observed effect on the addressing times and the threshold voltage is generally greater, the higher the total concentration of compounds of the formulae I to XV.

[0101] In a particularly preferred embodiment, the media according to the invention comprise compounds of the formulae II to IX (preferably II and/or III) in which X⁰ is OCF₃, OCHF₂, F, OCH═CF₂, OCF═CF₂, OCF₂CHFCF₃ or OCF₂—CF₂H. A favourable synergistic effect with the compounds of the formula I results in particularly advantageous properties.

[0102] The construction of the MLC display according to the invention from polarisers, electrode base plates and surface-treated electrodes corresponds to the conventional construction for displays of this type. The term conventional construction is broadly drawn here and also covers all derivatives and modifications of the MLC display, in particular including matrix display elements based on poly-Si TFTs or MIM.

[0103] A significant difference between the displays according to the invention and the hitherto conventional displays based on the twisted nematic cell consists, however, in the choice of the liquid-crystal parameters of the liquid-crystal layer.

[0104] The liquid-crystal mixtures which can be used in accordance with the invention are prepared in a manner conventional per se. In general, the desired amount of the components used in lesser amount is dissolved in the components making up the principal constituent, advantageously at elevated temperature. It is also possible to mix solutions of the components in an organic solvent, for example in-acetone, chloroform or methanol, and to remove the solvent again, for example by distillation, after thorough mixing.

[0105] The dielectrics may also comprise further additives known to the person skilled in the art and described in the literature, such as, for example, stabilisers and antioxidants. For example, 0-15% of pleochroic dyes or chiral dopants can be added.

[0106] C denotes a crystalline phase, S a smectic phase, S_(C) a smectic C phase, S_(B) a smectic B phase, N a nematic phase and I the isotropic phase.

[0107] V₁₀ denotes the voltage for 10% transmission (viewing angle perpendicular to the plate surface). t_(on) denotes the switch-on time and t_(off) the switch-off time at an operating voltage corresponding to 2 times the value of V₁₀. Δn denotes the optical anisotropy and n_(o) the refractive index. Δε denotes the dielectric anisotropy (Δε=ε_(∥)−ε_(⊥), where ε_(∥) denotes the dielectric constant parallel to the longitudinal molecular axes and ε_(⊥) the dielectric constant perpendicular thereto). The electro-optical data were measured in a TN cell at the 1 st minimum (i.e. at a d·Δn value of 0.5) at 20° C., unless expressly stated otherwise. The optical data were measured at 20° C., unless expressly stated otherwise.

[0108] In the present application and in the examples below, the structures of the liquid-crystal compounds are indicated by means of acronyms, the transformation into chemical formulae taking place in accordance with Tables A and B below. All radicals C_(n)H_(2n+1) and C_(m)H_(2m+1) are straight-chain alkyl radicals having n and m carbon atoms respectively. n and m are each, independently of one another, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14 or 15. The coding in Table B is self-evident. In Table A, only the acronym for the parent structure is indicated. In individual cases, the acronym for the parent structure is followed, separated by a dash, by a code for the substituents R¹, R², L¹ and L²: Code for R¹, R², L¹, L² R¹ R² L¹ L² nm C_(n)H_(2n+1) C_(m)H_(2m+1) H H nOm C_(n)H_(2n+1) OC_(m)H_(2m+1) H H nO.m OC_(n)H_(2n+1) C_(m)H_(2m+1) H H n C_(n)H_(2n+1) CN H H nN.F C_(n)H_(2n+1) CN H F nF C_(n)H_(2n+1) F H H nOF OC_(n)H_(2n+1) F H H nCl C_(n)H_(2n+1) Cl H H nF.F C_(n)H_(2n+1) F H F nF.F.F C_(n)H_(2n+1) F F F nCF₃ C_(n)H_(2n+1) CF₃ H H nOCF₃ C_(n)H_(2n+1) OCF₃ H H nOCF₂ C_(n)H_(2n+1) OCHF₂ H H nS C_(n)H_(2n+1) NCS H H rVsN C_(r)H_(2r+1)—CH═CH—C_(s)H_(2s)— CN H H rEsN C_(r)H_(2r+1)—O—C₂H_(2s)— CN H H nAm C_(n)H_(2n+1) COOC_(m)H_(2m+1) H H nOCCF₂.F.F C_(n)H_(2n+1) OCH₂CF₂H F F

[0109] Preferred mixture components are given in Tables A and B. TABLE A

[0110] TABLE B

[0111] TABLE C Table C shows possible dopants which are generally added to the mixtures according to the invention.

[0112] TABLE D Stabilisers which can be added, for example, to the mixtures according to the invention are mentioned below.

[0113] The following examples are intended to explain the invention without restricting it. Above and below, percentages are per cent by weight. All temperatures are given in degrees Celsius. m.p. denotes melting point, cl.p. clearing point. Furthermore, C=crystalline state, N=nematic phase, S=smectic phase and I=isotropic phase. The data between these symbols represent the transition temperatures. An denotes optical anisotropy (589 nm, 20° C.), AE the dielectric anisotropy (1 kHz, 20° C.). The flow viscosity ν₂₀ (mm²/sec) was determined at 20° C. The rotational viscosity γ₁ (mPa.s) was likewise determined at 20° C.

[0114] “Conventional work-up” means that water is added if necessary, the mixture is extracted with dichloromethane, diethyl ether, methyl tert-butyl ether or toluene, the phases are separated, the organic phase is dried and evaporated, and the product is purified by distillation under reduced pressure or crystallisation and/or chromatography. The following abbreviations are used:

[0115] n-BuLi 1.6 molar solution of n-butyllithium in n-hexane

[0116] DMAP 4-(dimethylamino)pyridine

[0117] THF tetrahydrofuran

[0118] DCC N,N′-dicyclohexylcarbodiimide

[0119] LDA lithium dimethylamide

EXAMPLE 1

[0120]

[0121] Step 1.1

[0122] 0.6 mol of A is dissolved in 750 ml of abs. THF and cooled to −70° C. After addition of 0.583 mol of lithium diisopropylamide, the mixture is stirred for 1 hour. CO₂ (1.2 mol) is subsequently passed into the reaction solution at such a rate that the temperature is ≦−60° C. When the reaction is complete, the reaction solution is stirred with water at −10° C. and subsequently acidified using HCl. Finally, the mixture is subjected to conventional work-up.

[0123] Step 1.2

[0124] 0.156 mol of thionyl chloride is added to 0.078 mol of B. The reaction mixture is refluxed for 2 hours. The excess thionyl chloride is stripped off under reduced pressure.

[0125] Step 1.3

[0126] 0.078 mol of C is added dropwise to 0.074 mol of 1,3-propanedithiol at 0° C. under N₂ with stirring. 0.112 mol of trifluoromethanesulfonic acid is subsequently added dropwise at −5° C., and the mixture is stirred for 2 hours. 0.297 mol of acetic anhydride is added dropwise at 3° C. After addition of 150 ml of abs. diethyl ether, the mixture is stirred for 0.5 hour. The crystals are cooled to −40° C., stirred for 1 hour, filtered off with suction, washed with diethyl ether and dried under reduced pressure.

[0127] Step 1.4

[0128] A mixture of 7.9 ml of triethylamine and 7.8 g of 3,4,5-trifluorophenol in 70 ml of dichloromethane is added dropwise at −70° C. to 0.035 mol of D dissolved in 200 ml of dichloromethane. The mixture is stirred at −70° C. for 1 hour, 0.175 mol of triethylamine hydrofluoride is added dropwise to the reaction mixture, the mixture is stirred for a further 0.5 hour, and a solution of 9 ml of bromine in 80 ml of dichloromethane is added dropwise at −70° C. The reaction mixture is stirred at −70° C. for a further 1.5 hours and allowed to warm to 0° C., and 210 ml of water and 90 ml of 32% sodium hydroxide solution are added. When the neutralisation is complete, the organic phase is subjected to conventional work-up.

[0129] Step 1.5

[0130] 0.015 ml of sodium metaborate octahydrate is initially introduced in 24 ml of H₂O, 0.380 mol of bis(triphenyl)phosphinepalladium, 0.380 mol of hydrazinium hydroxide and 10 ml of THF are added, and the mixture is stirred for 5 minutes. 0.019 mol of 4-chlorophenylboronic acid in 38 ml of THF is added to the reaction mixture, which is warmed to 65° C. and refluxed overnight. The reaction mixture is allowed to cool to room temperature, water and methyl tert-butyl ether are added, and the mixture is subjected to conventional work-up.

[0131] C 71 I; Δn=0.1271; Δε=9.9; γ₁=68

EXAMPLE 2

[0132]

[0133] 0.2 mmol of bis(triphenylphosphine)palladium, 0.01 mol of H and 6 ml of abs. THF are added to 7.5 mol of sodium metaborate octahydrate in 12 ml of H₂O, and the mixture is stirred for 5 minutes. After 0.01 mol of G in 18 ml of abs. THF has been added, the mixture is refluxed overnight. The reaction mixture is allowed to cool to room temperature, methyl tert-butyl ether is added, and the mixture is subjected to conventional work-up. C 68 I; Δn=0.1020; Δε=10.6; γ=71

EXAMPLE 3

[0134]

[0135] 0.2 mmol of bis(triphenylphosphine)palladium, 0.01 mol of K and 6 ml of abs. THF are added to 7.5 mol of sodium metaborate octahydrate in 12 ml of H₂O, and the mixture is stirred for 5 minutes. After 0.01 mol of J in 18 ml of abs. THF has been added, the mixture is refluxed overnight. The reaction mixture is allowed to cool to room temperature, methyl tert-butyl ether is added, and the mixture is subjected to conventional work-up.

MIXTURE EXAMPLES EXAMPLE M1

[0136] F.F 10.80% Clearing point [° C.]: 81.9 BCH-5F.F 9.00% Δn [589 nm, 20° C.]: 0.100 ECCP-30CF₃ 4.50% Δε [1 kHz, 20° C.]: 5.7 ECCP-50CF₃ 4.50% γ₁ [mPa · s): 125 CBC-33F 1.80% CBC-53F 1.80% CBC-55F 1.80% PCH-6F 7.20% PCH-7F 5.40% CCP-20CF₃ 7.20% CCP-30CF₃ 10.80% CCP-40CF₃ 6.30% CCP-50CF₃ 9.90% PCH-5F 9.00% PUQU-Cl—F 10.00%

EXAMPLE M2

[0137] BCH-3F.F 10.80% Clearing point [° C.]: 79.4 BCH-5F.F 9.00% Δn [589 nm, 20° C.]: 0.0975 ECCP-30CF₃ 4.50% Δε [1 kHz, 20° C.]: 5.8 ECCP-50CF₃ 4.50% ν₂₀ [mm² · s⁻¹]: 14 CBC-33F 1.80% γ₁ [mPa · s): 117 CBC-53F 1.80% CBC-55F 1.80% PCH-6F 7.20% PCH-7F 5.40% CCP-20CF₃ 7.20% CCP-30CF₃ 10.80% CCP-40CF₃ 6.30% CCP-50CF₃ 9.90% PCH-5F 9.00% PUQU-F—F 10.00%

EXAMPLE M3

[0138] BCH-3F.F 10.80% Clearing point [° C.]: 72.3 BCH-5F.F 9.00% Δn [589 nm, 20° C.]: 0.0913 ECCP-30CF₃ 4.50% Δε [1 kHz, 20° C.]: 5.4 ECCP-50CF₃ 4.50% CBC-33F 1.80% CBC-53F 1.80% CBC-55F 1.80% PCH-6F 7.20% PCH-7F 5.40% CCP-20CF₃ 7.20% CCP-30CF₃ 10.80% CCP-40CF₃ 6.30% CCP-50CF₃ 9.90% PCH-5F 9.00% UQU-Br—F 10.00%

EXAMPLE M4

[0139] CCP-2F.F.F 10.00% S → N [° C.]: <−20 CCP-3F.F.F 10.00% Clearing point [° C.]: 82.0 CCP-20CF₃.F  6.00% Δn [589 nm, 20° C.]: 0.0950 CCP-30CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 163 CCP-20CF₃  6.0% V_(10,0,20) [V]: 1.22 CCP-30CF₃  8.0% CCP-40CF₃  7.00% CCP-50CF₃  8.00% PUQU-F—F  8.00% CGU-2-F 10.00% CGU-3-F 11.00% CCGU-3-F  4.00%

EXAMPLE M5

[0140] CCP-1F.F.F 3.00% S → N [° C.]: <−40 CCP-2F.F.F 10.00% Clearing point [° C.]: 83.0 CCP-3F.F.F 4.00% Δn [589 nm, 20° C.]: 0.0937 CCP-20CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 165 CCP-30CF₃.F 12.00% V_(10,0,20) [V]: 1.26 CCP-20CF₃ 8.00% CCP-30CF₃ 8.00% CCP-40CF₃ 5.00% CCP-50CF₃ 8.00% PUQU-F—F 7.00% CGU-2-F 11.00% CGU-3-F 7.00% CCGU-3-F 5.00%

EXAMPLE M6

[0141] PUQU-F—F 8.00% CCP-1F.F.F 8.50% CCZU-2-F 3.00% CCZU-3-F 13.00% CCP-30CF₃ 8.00% CCP-40CF₃ 4.00% CGZP-2-OT 6.00% CGZP-3-OT 1.80% PGU-2-F 2.70% CC-5-V 10.00% CC-3-V1 12.00% CCH-35 5.00% CC-3-V 18.00%

EXAMPLE M7

[0142] PCH-5F 3.20% Clearing point [° C.]: 90.0 CCP-20CF₂.F.F 17.04% Δε [1 kHz, 20° C.]: 8.6 CCP-30CF₂.F.F 16.00% CCP-50CF₂.F.F 17.04% CUP-2F.F 5.36% CUP-3F.F 5.36% CBC-33F 5.36% CBC-53F 5.36% CBC-55F 5.28% PUQU-F—F 20.00%

EXAMPLE M8

[0143] CCP-2F.F.F 10.00% Clearing point [° C.]: 85.0 CCP-3F.F.F 4.00% Δn [589 nm, 20° C.]: 0.0912 CCP-20CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 152 CCP-30CF₃.F 12.00% V_(10,0,20) [V]: 1.31 CCP-3F.F 12.00% CCP-30CF₃ 4.00% CCP-40CF₃ 5.00% CCP-50CF₃ 8.00% PUQU-F—F 7.00% CGU-2-F 11.00% CGU-3-F 7.00% PCH-7F 5.00% CBC-33 3.00%

EXAMPLE M9

[0144] CCP-2F.F.F 10.00% Clearing point [° C.]: 99.0 CCP-3F.F.F 4.00% Δn [589 nm, 20° C.]: 0.0979 CCP-20CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 186 CCP-30CF₃.F 12.00% V_(10,0,20) [V]: 1.32 CCP-3F.F 12.00% CCP-30CF₃ 4.00% CCP-40CF₃ 5.00% CCP-50CF₃ 5.00% PUQU-Cl—F 7.00% CGU-2-F 11.00% PCH-7F 5.00% CBC-33 6.00% CCGU-3-F 7.00%

EXAMPLE M10

[0145] CCP-2F.F.F 10.00% Clearing point [° C.]: 98.0 CCP-3F.F.F 4.00% Δn [589 nm, 20° C.]: 0.0975 CCP-20CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 184 CCP-30CF₃.F 12.00% V_(10,0,20) [V]: 1.29 CCQU-3-F 10.00% CCP-30CF₃ 4.00% CCP-40CF₃ 5.00% CCP-50CF₃ 5.00% PUQU-Cl—F 7.00% CGU-2-F 11.00% PCH-7F 5.00% CBC-33 6.00% CCGU-3-F 9.00%

EXAMPLE M11

[0146] CCQU-1-F 10.00% Clearing point [° C.]: 86.0 CCQU-2-F 4.00% Δn [589 nm, 20° C.]: 0.0928 CCP-20CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 152 CCP-30CF₃.F 12.00% V_(10,0,20) [V]: 1.34 CCQU-3-F 10.00% CCP-30CF₃ 4.00% PUQU-F—F 7.00% CGU-2-F 11.00% PCH-7F 5.00% CBC-33 6.00% CCGU-3-F 9.00% CC-3-V1 10.00%

EXAMPLE M12

[0147] IS-9003 10.00% Clearing point [° C.]: 85.0 CCP-3F.F.F 10.00% Δn [589 nm, 20° C.]: 0.1015 CCP-20CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 145 CCP-30CF₃.F 12.00% V_(10,0,20) [V]: 1.33 CCP-30CF₃ 4.00% PUQU-F—F 7.00% CGU-2-F 11.00% PCH-7F 5.00% CBC-33 6.00% CCGU-3-F 9.00% CC-3-V1 10.00% CCOC-4-3 4.00%

EXAMPLE M13

[0148] IS-9003 10.00% Clearing point [° C.]: 71.0 CCP-3F.F.F 10.00% Δn [589 nm, 20° C.]: 0.0980 CCP-20CF₃.F 12.00% γ₁ [mPa · s, 20° C.): 125 CCP-30CF₃.F 12.00% V_(10,0,20) [V]: 1.36 CCP-30CF₃ 4.00% PUQU-Cl—F 11.00% CGU-2-F 11.00% CC-3-V 6.00% CCGU-3-F 9.00% CC-3-V1 10.00% CCOC-4-3 5.00% 

1. Liquid-crystalline compounds of the formula I

in which X¹ and X² are each, independently of one another, F, Cl, Br or I, or one of the radicals X¹ and X² is alternatively H, X³ is F, Cl, CN, NCS, SF₅, or a halogenated alkyl, alkoxy, alkenyl or alkenyloxy radical having up to 5 carbon atoms, Z¹ and Z² are each, independently of one another, —CO—O—, —O—CO—, —CF₂O—, —OCF₂—, —CH₂O—, —OCH₂—, —CH₂CH₂—, —(CH₂)₄—, —C₂F₄—, —CH₂CF₂—, —CF₂CH₂—, —CF═CF—, —CH═CH—, —C≡C— or a single bond, with the proviso that at least one of the bridges Z¹ and Z² is —CF₂O— or —OCF₂—, a is 0, 1 or 2, and L¹ to L¹¹ are each, independently of one another, H or F.
 2. Liquid-crystalline compounds according to claim 1, characterised in that X¹═F or Cl and X²═H and X³═F or OCF₃.
 3. Liquid-crystalline compounds according to claim 1, characterised in that a=1.
 4. Liquid-crystalline compounds according to claim 1, characterised in that L¹ is fluorine and L² is fluorine or hydrogen.
 5. Liquid-crystalline compounds according to claim 4, characterised in that L² and L³ are fluorine.
 6. Liquid-crystalline compounds of the formulae I1 to I120


7. Liquid-crystalline medium comprising at least two mesogenic compounds characterised in that it comprises at least one compound of the formula I according to claim
 1. 8. Liquid-crystalline medium according to claim 7, characterised in that it comprises one or more compounds selected from the group consisting of the general formulae II to IX

in which R⁰ is H, n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 carbon atoms, X⁰ is F, Cl, halogenated alkyl, halogenated alkenyl, halogenated alkenyloxy or halogenated alkoxy having up to 7 carbon atoms, Z⁰ is —CH═CH—, —C₂H₄—, —(CH₂)₄—, —C₂F₄—, —CH₂O—, —OCH₂—, —CF═CF—, —CF₂O—, —OCF₂—or —COO—, Y¹, Y², Y³ and Y⁴ are each, independently of one another, H or F, and r is 0 or
 1. 9. Use of the liquid-crystalline medium according to claim 7 for electro-optical purposes.
 10. Electro-optical liquid-crystal display containing a liquid-crystalline medium according to claim
 7. 11. Use of the liquid-crystalline compounds according to claim 1 as synthetic building blocks, crop-protection agents, as pharmaceuticals and as components in liquid-crystalline media. 